This group of ferrites is used in devices, which must have low magnetic and dielectric losses at dm- and cm- wave range.
|
Types |
4pMs
(G)
±5% |
ΔH
(-3dB)
(Oe) |
ε'
±5% |
tgδε
•104 |
geff
±3% |
Tc
(oC)
nominal |
ΔHk
(Oe)
nominal |
Hc
(Oe)
nominal |
Br
(G)
nominal |
α Ms
(% • oC-1)
(-60÷+85)oC |
|
3CH15 |
2100 |
≤380 |
13.0 |
≤8 |
2.06 |
360 |
- |
- |
1550 |
-0.15 |
|
3CH7 |
1700 |
≤390 |
12.3 |
≤6 |
- |
260 |
7.5 |
5.5 |
1030 |
-0.30 |
|
3CH17 |
1600 |
≤680 |
12.5 |
≤2.5 |
2.10 |
350 |
- |
4.5 |
- |
-0.19 |
|
6CH1 |
1450 |
≤180 |
12.0 |
≤4 |
2.02 |
140 |
- |
1.1 |
920 |
-0.47 |
|
8CH5B |
1050 |
≤430 |
10.5 |
≤2 |
1.98 |
330 |
6.0 |
1.0 |
- |
-0.17 |
|
40CH |
880 |
≤110 |
10.2 |
≤20 |
- |
90 |
- |
0.9 |
400 |
-1.03 |
|
10CH15 |
780 |
≤250 |
10.0 |
≤4 |
- |
160 |
6.0 |
2.0 |
- |
-0.52 |
|
10CH8 |
700 |
≤220 |
9.5 |
≤25 |
- |
140 |
- |
2.0 |
560 |
-0.57 |
Frequency of measurement ΔH, ΔHk, ε’, tgδε - 9.4 GHz.
Lithium – Titanium – Zinc Spinels
Li – Ti – Zn
This group of ferrites has low non resonant magnetic losses, good squareness of hysteresis loop and high Curie temperature. They are mostly used in non resonant controlled devices of low power levels at cm- and mm- wave ranges (phase shifters, switches, etc.).
|
Types |
4pMs
(G)
±5% |
ΔH
(-3dB)
(Oe) |
ε'
±5% |
tgδε
• 104 |
geff
±3% |
Tc
(oC)
nominal |
ΔHk
(Oe)
nominal |
Hc
(Oe)
nominal |
Br
(G)
nominal |
αMs
(% • oC-1)
(-60÷+85)oC |
|
1CH11 |
4750 |
≤300 |
14.6 |
≤6 |
2.06 |
450 |
3.0 |
1.1 |
3250 |
-0.15 |
|
1CH12B1 |
4500 |
≤300 |
15.1 |
≤5 |
2.20 |
520 |
3.0 |
1.1 |
3250 |
-0.11 |
|
1CH13 |
4000 |
≤460 |
15.0 |
≤6 |
2.06 |
570 |
2.0 |
1.4 |
2600 |
-0.09 |
|
3CH34M |
3500 |
≤300 |
15.9 |
≤5 |
2.05 |
430 |
2.0 |
1.0 |
2450 |
|
|
2CH10 |
3150 |
≤500 |
15.5 |
≤4 |
2.05 |
560 |
2.0 |
1.5 |
2150 |
-0.08 |
|
2CH10M |
3000 |
≤300 |
16.1 |
≤5 |
2.05 |
420 |
2.0 |
1.0 |
2050 |
|
|
3CH27Ì |
2500 |
≤300 |
16.4 |
≤5 |
2.05 |
410 |
2.0 |
1.0 |
1750 |
|
|
3CH23 |
2250 |
≤350 |
16.3 |
≤5 |
2.04 |
430 |
2.2 |
1.1 |
1650 |
-0.16 |
|
3CH26 |
2100 |
≤330 |
16.3 |
≤7 |
2.00 |
430 |
2.0 |
1.2 |
1500 |
-0.19 |
|
3CH19B |
2000 |
≤430 |
16.2 |
≤5 |
2.02 |
440 |
1.6 |
1.3 |
1450 |
-0.13 |
|
3CH19Ì |
2000 |
≤150 |
16.9 |
≤5 |
2.04 |
245 |
1.6 |
0.52 |
1160 |
- |
|
3CH19B1* |
2050 |
≤430 |
16.2 |
≤5 |
2.02 |
440 |
1.6 |
1.3 |
1500 |
-0.13 |
|
3CH18 |
1870 |
≤410 |
16.5 |
≤8 |
2.04 |
300 |
1.6 |
1.1 |
1200 |
-0.18 |
|
4CH14B |
1550 |
≤420 |
16.6 |
≤5 |
2.05 |
390 |
1.5 |
1.1 |
1100 |
-0.17 |
|
4CH14Ì |
1500 |
≤150 |
17.3 |
≤5 |
2.01 |
210 |
1.6 |
0.52 |
940 |
- |
|
6CH2 |
1200 |
≤300 |
17.0 |
≤4 |
1.98 |
300 |
1.5 |
1.0 |
780 |
-0.12 |
|
8CH6 |
1000 |
≤360 |
17.0 |
≤4 |
1.98 |
300 |
1.5 |
1.4 |
680 |
-0.15 |
Frequency of measurement ΔH, ΔHk, ε’, tgδε - 9.4 GHz.
*Type 3CH19B1 has ultra-moisture resistance (water absorption W ≤ 0.1%).
Nickel – Zinc Spinels
Ni – Zn
The spinels of this group feature high Curie temperature. They are widely used in resonance devices operating at cm- and mm- wave ranges.
|
Types |
4pMs
(G)
±5% |
ΔH
(-3dB)
(Oe) |
ε'
±5% |
tgδε
• 104 |
geff
±3% |
Tc
(oC)
nominal |
ΔHk
(Oe)
nominal |
Hc
(Oe)
nominal |
Br
(G)
nominal |
αMs
(% • oC-1)
(-60÷+85)oC |
|
1CH9 |
5000 |
≤150 |
13.6 |
≤6 |
2.11 |
345 |
6.0 |
1.5 |
3500 |
-0.21 |
|
1CH4 |
4750 |
≤210 |
13.4 |
≤6 |
2.14 |
400 |
4.5 |
2.0 |
3150 |
-0.17 |
|
1CH16 |
4750 |
≤170 |
13.7 |
≤5 |
2.11 |
325 |
10.0 |
1.0 |
2850 |
-0.23 |
|
1CH10 |
4500 |
≤210 |
13.5 |
≤6 |
2.13 |
430 |
7.7 |
1.0 |
3100 |
-0.13 |
|
2CH6 |
4000 |
≤240 |
13.7 |
≤4 |
2.12 |
480 |
7.0 |
1.9 |
2400 |
-0.08 |
|
2CH7 |
3500 |
≤360 |
13.5 |
≤6 |
2.21 |
540 |
6.0 |
3.8 |
2430 |
-0.07 |
|
2CH11 |
3150 |
≤300 |
13.7 |
≤4 |
2.20 |
560 |
7.0 |
3.0 |
2000 |
-0.09 |
|
1CH2B |
2850 |
≤300 |
13.8 |
≤5 |
2.20 |
550 |
8.0 |
3.0 |
1200 |
-0.10 |
|
3CH21 |
2500 |
≤270 |
13.7 |
≤5 |
2.20 |
530 |
9.0 |
3.5 |
1100 |
-0.11 |
|
4CH10B |
2300 |
≤200 |
13.6 |
≤6 |
2.20 |
500 |
10.0 |
3.5 |
900 |
-0.13 |
Frequency of measurement ΔH, ΔHk, ε’, tgδε - 9.4 GHz.
High density Nickel – Zinc Spinels
Ni – Zn
High density ferrites are designed for microstrip microwave devices as substrates.
|
Types |
4pMs
(G)
±5% |
ΔH
(-3dB)
(Oe) |
ε'
±5% |
tgδε
• 104 |
geff
±3% |
Tc
(oC)
nominal |
ΔHk
(Oe)
nominal |
Hc
(Oe)
nominal |
Br
(G)
nominal |
αMs
(% • oC-1)
(-60÷+85)oC |
|
1CH91 |
5100 |
≤130 |
14.0 |
≤4 |
2.11 |
345 |
6.0 |
1.5 |
3500 |
-0.21 |
|
1CH41 |
4900 |
≤190 |
13.9 |
≤4 |
2.14 |
400 |
4.5 |
2.0 |
3150 |
-0.17 |
|
1CH161 |
4900 |
≤140 |
13.9 |
≤5 |
2.11 |
325 |
10.0 |
1.0 |
2850 |
-0.23 |
|
1CH101 |
4600 |
≤200 |
13.7 |
≤4 |
2.13 |
430 |
7.7 |
1.0 |
3100 |
-0.13 |
|
2CH61 |
4100 |
≤230 |
13.8 |
≤4 |
2.12 |
480 |
7.0 |
1.9 |
2400 |
-0.08 |
|
2CH71 |
3600 |
≤330 |
13.7 |
≤4 |
2.21 |
540 |
6.0 |
3.8 |
2430 |
-0.07 |
|
2CH111 |
3200 |
≤270 |
13.9 |
≤4 |
2.20 |
560 |
7.0 |
3.0 |
2000 |
-0.09 |
|
1CH2B1 |
2900 |
≤270 |
14.0 |
≤5 |
2.20 |
550 |
8.0 |
3.0 |
1200 |
-0.10 |
|
3CH211 |
2500 |
≤250 |
13.9 |
≤4 |
2.20 |
530 |
9.0 |
3.5 |
1100 |
-0.11 |
|
4CH10B1 |
2300 |
≤170 |
13.8 |
≤5 |
2.20 |
500 |
10.0 |
3.5 |
900 |
-0.13 |
Frequency of measurement ΔH, ΔHk, ε’, tgδε - 9.4 GHz.
Ferrite spinels 